Capacitor Dimensions:
|
Dimension Size |
L
|
W
|
| 0402 (1005 type) |
1.0
+/- 0.05
|
0.5
+/- 0.05
|
| 0603 (1608 type) |
1.6
+/- 0.15
|
0.8
+/- 0.1
|
| 0805 (2012 type) |
2.0
+/- 0.2
|
1.25
+/- 0.2
|
| 1206 (3216 type) |
3.2
+/- 0.2
|
1.6
+/- 0.2
|
| 1210 (3225 type) |
3.2
+/- 0.3
|
2.5
+/- 0.2
|
| 1812 (4532 type) |
4.5
+/- 0.4
|
3.2
+/- 0.3
|
| 2220 (5750 type) |
5.7
+/- 0.4
|
5.0
+/- 0.3
|
Dielectric and Specification:
NPO
|
Capacitance:
|
<=1,000pF,
1MHz+/-10%, 1Vrms
>1,000pF, 1KHz+/-10%, 1Vrms |
||
|
Operating
Temperature:
|
-55
¢J to +125 ¢J
|
||
|
Temperature
Coefficient:
|
¡µC
= 0 +/- 30 ppm/¢J
|
||
|
Voltage:
|
50Vdc
and 100Vdc
|
||
|
D.F/Q
value:
|
DF
= 0.1% max.
<30pF: Q >= 400+20C >=30pF: Q >= 1,000 |
||
|
I.R
|
100G£[
or 1000£[F minimum, whichever is smaller. The apply rated voltage
for max. of 2 min. with 50mA limiting current at 25¢J
|
||
|
Solderablity:
|
75%
min. covered with smooth and bright solder coating under 230+/-5¢J
solder bath for 4 +/- 1s dipping time.
|
||
|
Dielectric
Strength:
|
250%
of rated Vdc for 5s with charging current less than 50mA
|
||
|
Resistance
to Leaching:
|
20%
of the metallization of the head face may be missing under 260+/-5¢J
solder bath for 30+/-1.0s dipping time.
|
||
|
Humidity:
|
500
hours at 40 +/- 2¢J under 90 to 95% humidity. |
||
|
Load
Life:
|
200%
rated voltage at +125¢J for 1000 hours, Measurement shall be taken
after 24 hrs stablization. |
||
|
Aging
Rate:
|
0%
per decade hour
|
||
|
Tolerance:
|
C
= +/-0.25pF
|
D
= +/-0.5pF
|
F
= +/-1.0%
|
|
G
= +/-2.0%
|
J
= +/-5.0%
|
K
= +/-10%
|
|
|
Capacitance:
|
1KHz+/-10%, 1Vrms
|
||
|
Operating
Temperature:
|
-55
¢J to +125 ¢J
|
||
|
Temperature
Coefficient:
|
¡µC
= +/- 15% max.
|
||
|
Voltage:
|
16Vdc,
25Vdc, 50Vdc and 100Vdc
|
||
|
D.F/Q
value:
|
DF
= 2.5% max. for 25V, 50V and 100V
DF = 3.5% max. for 16V |
||
|
I.R
|
100G£[
or 1000£[F minimum, whichever is smaller. The apply rated voltage
for max. of 2 min. with 50mA limiting current at 25¢J
|
||
|
Solderablity:
|
75%
min. covered with smooth and bright solder coating under 230+/-5¢J
solder bath for 4 +/- 1s dipping time.
|
||
|
Dielectric
Strength:
|
250%
of rated Vdc for 5s with charging current less than 50mA
|
||
|
Resistance
to Leaching:
|
20%
of the metallization of the head face may be missing under 260+/-5¢J
solder bath for 30+/-1.0s dipping time.
|
||
|
Humidity:
|
500
hours at 40 +/- 2¢J under 90 to 95% humidity. |
||
|
Load
Life:
|
200%
rated voltage at +125¢J for 1000 hours, Measurement shall be taken
after 24 hrs stablization. |
||
|
Aging
Rate:
|
3.0%
per decade hour
|
||
|
Tolerance:
|
J
= +/-5%
|
K
= +/-10%
|
M
= +/-20%
|
|
Capacitance:
|
1KHz+/-10%, 1Vrms
|
|
|
Operating
Temperature:
|
-30
¢J to +85 ¢J
|
|
|
Temperature
Coefficient:
|
¡µC
= + 22% to - 82%
|
|
|
Voltage:
|
16Vdc,
25Vdc, and 50Vdc
|
|
|
D.F/Q
value:
|
DF
= 5.0% max. for 25V, and 50V
DF = 7.0% max. for 16V |
|
|
I.R
|
10G£[
or 500£[F minimum, whichever is smaller. The apply rated voltage
for max. of 2 min. with 50mA limiting current at 25¢J
|
|
|
Solderablity:
|
75%
min. covered with smooth and bright solder coating under 230+/-5¢J
solder bath for 4 +/- 1s dipping time.
|
|
|
Dielectric
Strength:
|
250%
of rated Vdc for 5s with charging current less than 50mA
|
|
|
Resistance
to Leaching:
|
20%
of the metallization of the head face may be missing under 260+/-5¢J
solder bath for 30+/-1.0s dipping time.
|
|
|
Humidity:
|
500
hours at 40 +/- 2¢J under 90 to 95% humidity. |
|
|
Load
Life:
|
200%
rated voltage at +85¢J for 1000 hours, Measurement shall be taken
after 24 hrs stablization. |
|
|
Aging
Rate:
|
7.0%
per decade hour
|
|
|
Tolerance:
|
M
= +/-20%
|
Z
= +80/-20%
|
|
Size
Code |
L
|
W
|
T
|
Lead
Diameter(G)
|
Lead
Length(L)
|
Lead
Spacing(S)
|
Lead
Styles
|
|
R15
|
0.15
(3.81) |
0.150
(3.81) |
0.100
(2.54) |
0.02
(0.50) |
0.1(2.5)
to
1.0(25) |
0.1(2.54)
|
L
|
|
0.2(5.08)
|
H,
K, A
|
||||||
|
0.3(7.62)
|
H
|
||||||
|
R20
|
0.200
(5.08) |
0.200
(5.08) |
0.125
(3.18) |
0.02
(0.50) |
0.1(2.5)
to
1.0(25) |
0.1(2.54)
|
L,
K
|
|
0.2(5.08)
|
H,
K
|
||||||
|
0.25(6.35)
|
H
|
||||||
|
0.3(7.62)
|
H
|
||||||
|
R30
|
0.300
(7.62) |
0.300
(7.62) |
0.150
(3.81) |
0.02
(0.05) |
0.1(2.5)
to
1.0(25) |
0.2(5.08)
|
H
|
|
0.3(7.62)
|
H
|
|
Color
|
Size
Code
|
Capacitance
|
Tolerance
|
Rated
Voltage
|
Temp.
Char.
|
|
Blue
|
R15,R20,R30
|
V
|
--
|
--
|
--
|
|
Yellow
|
R15
|
V
|
--
|
--
|
--
|
|
Yellow
|
R20,R30
|
V
|
V
|
V
|
V
|
First line -- Capacitance value.
Second line -- Tol. WVdc, and T.C
| Order according to customer design of size, appearance and raw material. | |
| Standard Size: | Diameter--
0.3 mm to 1.5 mm Leagth -- 3.0 mm to 80.0 mm |
| Raw material: | Nickel
plated OFC., Silver plated OFC., with silver content copper alloy and nickel plating, with silver content copper alloy and silver plating. |
| Packing: | Loose
packing -- 5Kpcs to 50Kpcs per box 160 box per carton. |
| Material: | Paper or Plastic |
| Commodity: | >
Top cover tape for punched Carrier Tape. > Unpunched Carrier Tape. > Bottom Cover Tape for punched Carrier Tape. |